摘要：介紹了以70％～75％ TiO2的低品位高鈦渣為原料制備人造金紅石的分離工藝.低品位高鈦渣中MgO,FeO,CaO,Al2O3和SiO2進入雜質(zhì)相,鈦組分進入金紅石相,金紅石相中TiO2品位達到90％～95％,可滿足流態(tài)化氯化對雜質(zhì)的要求.1 050℃的低溫預氧化與1 510℃的高溫熱處理促使渣中分散于各礦物相的鈦組分選擇性轉(zhuǎn)移并富集于金紅石相,金紅石相析出與長大,用稀硫酸和稀鹽酸實現(xiàn)金紅石相的分離.實驗結果表明,金紅石礦物相平均晶粒度可以達到25 μrn,通過稀酸選擇性浸出改性渣,可以獲得95％TiO2品位的人造金紅石.Abstract：A new technique was developed for the conversion of high titania slag,containing 70％-75％ TiO2 and with MgO,FeO,CaO,Al2O3 and SiO2 as main impurities,into a synthetic rutile,90％-95％ TiO2,which satisfies the requirements for fluidizing chlorination process with respect to impurity contents.After a pre-oxidation at around 1 042 ℃ and a heat-treatment above 1 510 ℃,the Ti components in high titania slag can be enriched into the rutile phase which can precipitate and grow,and can be separated with dilute hydrochloric and sulfuric acid,respectively.The results show that the average crystal size of rutile phase is over 25 μm,and the synthetic rutile containing more than 95％ TiO2 can be produced by selective leaching. 作者： 張力[1] 李光強[2] 張武[1] Author： ZHANG Li[1] LI Guang-qiang[2] ZHANG Wu[1] 作者單位： 東北大學材料與冶金學院,沈陽,110004武漢科技大學材料與冶金學院,武漢,430081 期 刊： 中國有色金屬學報（英文版） ISTICEISCI Journal： Transactions of Nonferrous Metals Society of China 年，卷(期)： 2011, 21(10) 分類號： Q51 關鍵詞： 高鈦渣 氧化 浸出 金紅石 Keywords： high titania slag oxidation leaching rutile 機標分類號： TQ1 TU5 機標關鍵詞： 低品位 高鈦渣 原料制備 金紅石相 high TiO2 人造金紅石 average crystal size sulfuric acid new technique 礦物相 選擇性轉(zhuǎn)移 選擇性浸出 平均晶粒度 高溫熱處理 低溫預氧化 Al2O3 質(zhì)的要求 實驗結果 分離工藝 基金項目： the Open Research Fund of Key Laboratory for Ferrous Metallurgy and Resources Utilizati 低品位高鈦渣中鈦組分制備金紅石[期刊論文] 中國有色金屬學報（英文版） --2011, 21(10)張力 李光強 張武介紹了以70％～75％ TiO2的低品位高鈦渣為原料制備人造金紅石的分離工藝.低品位高鈦渣中MgO,FeO,CaO,Al2O3和SiO2進入雜質(zhì)相,鈦組分進入金紅石相,金紅石相中TiO2品位達到90％～95％,可滿足流態(tài)化氯化對雜質(zhì)的要求.1 050℃的低...【低品位高鈦渣中鈦組分制備金紅石】相關文章：
鈦鈦鈦04-29
含鈦高爐渣綜合利用與鈦組分析出技術的進展05-02
鈦04-29
高純金屬鈦中微量氫的分析方法研究04-29
鈦螺絲04-29
鈦法蘭04-29
高鈦礦渣的粉磨特性研究04-27
從赤泥中浸出鈦的研究04-26
鈦材加工04-29