廢舊電視機外殼的熱解動力學研究

摘要： 采用熱重分析儀對含有八溴聯(lián)苯醚的電視機外殼(紅外分析鑒定為高抗沖聚苯乙烯,high impact styrene, HIPS)進行了真空條件下的熱失重實驗,研究了不同升溫速率下廢舊阻燃高抗沖聚苯乙烯的降解特性、熱解動力學,結果表明樣品的熱化學特征參數(shù)隨升溫速率的提高而明顯增大.根據(jù)Arrhenius定律和Friedman方法分析研究了對象的熱解動力學,所得相關系數(shù)均在0.98以上.該研究的結果為廢舊高抗沖聚苯乙烯塑料和其他廢舊電子電氣塑料的資源化、無害化利用提供了可靠的理論參考. Abstract： The pyrolysis of flame retarded TV housings (high impact polystyrene, HIPS) containing octabromodiphenyl ether (O8BDE) was performed under vacuum condition to understand the decomposition behavior. The decomposition temperatures of O8BDE and cracking temperatures of plastics under different heating rates (5 K/min,10 K/min,20 K/min and 40 K/min) were obtained. Analyzing the kinetic parameters with Arrhenius law and Friedman method, the correlating coefficients are all above 0.98. The results obtained in this study provide references for innoxiously recycling HIPS plastic wastes and other wastes of electrical and electronic equipment (WEEE) plastics. 作 者： 陳源    陳烈強    黃華杰    CHEN Yuan    CHEN Lie-qiang    HUANG Hua-jie   作者單位： 華南理工大學化學與化工學院傳熱強化與過程節(jié)能教育部重點實驗室,廣東,廣州,510640  期 刊： 陜西科技大學學報（自然科學版）  ISTIC   Journal： JOURNAL OF SHAANXI UNIVERSITY OF SCIENCE AND TECHNOLOGY(NATURAL SCIENCE EDITION)  年，卷(期)： 2008, 26(4)  分類號： X705 TQ013.2  關鍵詞： 高抗沖聚苯乙烯    多溴聯(lián)苯醚    真空裂解    動力學    Keywords： HIPS    polybromodiphenyl ether    vacuum pyrolysis    kinetic   

【廢舊電視機外殼的熱解動力學研究】相關文章：

苦澀的外殼作文10-15

Zippo外殼代碼完全版07-26

讓廢舊電池回家02-26

電視機作文07-28

未解之謎何時解_700字05-02

廢舊電池的危害作文09-21

讓廢舊電池回家作文09-13

電視機的變遷作文09-19

電視機的私語作文10-05

電視機的自述的作文08-06